Osteoblast adhesion on nanophase ceramics.

Webster TJ, Siegel RW, Bizios R. Biomaterials. 1999 Jul;20(13):1221-7.

Abstract

Osteoblast adhesion on nanophase alumina (Al2O3) and titania (TiO2) was investigated in vitro. Osteoblast adhesion to nanophase alumina and titania in the absence of serum from Dulbecco’s modified Eagle medium (DMEM) was significantly (P < 0.01) less than osteoblast adhesion to alumina and titania in the presence of serum. In the presence of 10% fetal bovine serum in DMEM osteoblast adhesion on nanophase alumina (23 nm grain size) and titania (32 nm grain size) was significantly (P < 0.05) greater than on conventional alumina (177 nm grain size) and titania (2.12 microm grain size), respectively, after 1, 2, and 4 h. Further investigation of the dependence of osteoblast adhesion on alumina and titania grain size indicated the presence of a critical grain size for osteoblast adhesion between 49 and 67 nm for alumina and 32 and 56 nm for titania. The present study provides evidence of the ability of nanophase alumina and titania to simulate material characteristics (such as surface grain size) of physiological bone that enhance protein interactions (such as adsorption, configuration, bioactivity, etc.) and subsequent osteoblast adhesion.

Link: ScienceDirect